胶管钢丝用C72DA热轧盘条的开发与应用

胶管钢丝用C72DA热轧盘条的开发与应用

曹树卫1,2,王新江,康永林 21

(1.北京科技大学材料科学与工程学院,北京100083;

2.安阳钢铁集团有限责任公司,河南安阳455004

摘要:介绍了安钢试制的高压胶管钢丝用C72DA盘条的成分设计、工艺控制要点及应用情况,分析了试验钢的中心偏析、显微组织和夹杂物,并与同类钢种的应用情况进行了对比。结果表明,试制盘条的微观组织、拉拔性能均达到了用户的使用要求。

关键词:高碳钢盘条;微观组织;夹杂物;表面质量;拉拔

中图分类号:TG335.63:TGl42.1 文献标识码:B 文章编号:1003—9996(2010)04--0065—03

Development and Application of C72DA Wire Rod for High—pressure Hose

CAO Shu~wei,WANG Xin-jiang,KANG Yong-lin

(1.School of Materials Science 8L Engineering,University of Science&Technology Beijing,

Beijing 100083,China

2.Anyang Iron&Steel Group Co.,Ltd.,Anyang 455004,China)

Abstract:The composition design,processes control key points and application effect of C72DA wire rod for high-pressure hose were introduced.The center segregation,

microstructures and inclusions of this steel were analyzed,and the application situation was compared with the same steel produced by other enterprise.The resuits indicated that the microstructure and drawing property of this steel could be met the need of user. Key words:high carbon wire rod; microstructure;inclusions;surface quality;drawing

随着我国交通运输的发展,子午线轮胎用钢

帘线、高压胶管钢丝、胎圈钢丝的需求量越来越

大,为此安阳钢铁集团有限责任公司开发了胶管

钢丝用C72DA热轧盘条,其采用洁净钢生产工

艺,节能环保,环境效益良好。

1胶管钢丝用钢化学成分

C72DA高碳钢盘条主要用于制作胶管和钢帘线等冷拉钢丝(直径小于00.8ram),其化学成分控制范围窄,且要求中心偏析小,钢质纯净,有害元素S、P、Cu含量低。这是由于中心偏析和成分波动会引起盘条的通条性能不均匀,易造成断丝;而有害元素S含量过高,产品塑性、韧性降低,并会引起热裂,P含量过高会降低塑性、造成冷脆,Cu含量高则会引起红脆D-33。另外,Mn、Cr、Ni等元素会影响热处理工艺和产品性能,Ti对钢丝的抗疲劳性能影响较大,Ti、Al和氧、氮结合生成氧化铝、氮化钛等脆性夹杂会影响到产品的加工工艺性能¨]。因此,设计试验钢化学成分见表1。此外,连铸坯的质量对最终产品性能有很大影响,铸坯内部中心区要致密(疏松、缩孔要小),铸坯中心偏析要小。安钢要求C72DA盘条中心偏析不大于3级。 [5]l,22l